Comportamiento a la corrosión atmosférica marina de aceros autopatinables con estructura ferrítico perlítica y ferrítico martensítica

Artigas, Alfredo y Bustos, Oscar y Sipos, Konstantin y Garza Montes de Oca, Nelson Federico y Monsalve G., Alberto y Mena, Juan y Seco, Rodrigo (2015) Comportamiento a la corrosión atmosférica marina de aceros autopatinables con estructura ferrítico perlítica y ferrítico martensítica. Matéria (Rio de Janeiro), 20 (3). pp. 659-667. ISSN 1517-7076

[img]
Vista previa
Texto
163.pdf - Versión Publicada
Available under License Creative Commons Attribution Non-commercial No Derivatives.

Download (541kB) | Vista previa

Resumen

La industria del acero se encuentra constantemente enfrentada al desafío del desarrollo de nuevos y mejores aceros para diversas necesidades, tales como la necesidad de aceros estructurales con mayor resistencia a la corrosión marina que los que existen en la actualidad, y que además posean una mayor resistencia mecánica. Por ello y en pos de lo anteriormente expuesto es evidente que, investigar en forma sistemática tanto la influencia de los elementos aleantes, como las variables del proceso de fabricación de aceros estructurales resistentes a la corrosión marina es relevante para el desarrollo del mercado acerero nacional. El presente trabajo tendrá por objetivo, la comparación de comportamiento a la corrosión atmosférica marina (espesor corroído en el tiempo) entre aceros de composición autopatinable (ASTM A242 y ASTM A588) con estructuras ferrítico-perlítica y ferrítico-martensítica. Para lo anterior se realizaron ciclos de humectación salina y secado. La humectación salina se realizó en cámara de niebla salina, de acuerdo a los requerimientos presentados en la norma ASTM B177, y el secado, en una mufla a 40 °C. Tras el retiro de muestras, se realizaron decapados químicos, según lo requerido en ASTM G1, para la determinación de espesor corroído. ABSTRACT The steel industry constantly faces the challenge of developing new and better steels for diverse needs, on of this necessities is the use of structural steels with higher corrosion resistance to marine atmospheres and improved mechanical properties than those that currently exist. Therefore, it is necessary to systematically research both the influence in the corrosion resistant to marine atmospheres of the alloying elements, and others variables such as changes in the manufacturing process of this materials. This work aims to compare the behavior on marine atmospheric corrosion between weathering steels (ASTM A242 and ASTM A588) with ferritic-pearlitic and ferritic-martensitic structures. Wetting and drying cycles were performed. Saline wetting was performed in a salt spray apparatus, according to ASTM B177, while drying was performed in a furnace at 40°C. At the end of each cycles, the corrosion products were removed in accordance to ASTM G1.

Tipo de elemento: Article
Palabras claves no controlados: Ambiente marino, Corrosión acelerada, Aceros autopatinables.
Divisiones: Ingeniería Mecánica y Eléctrica
Usuario depositante: Editor Repositorio
Creadores:
CreadorEmailORCID
Artigas, AlfredoNO ESPECIFICADONO ESPECIFICADO
Bustos, OscarNO ESPECIFICADONO ESPECIFICADO
Sipos, KonstantinNO ESPECIFICADONO ESPECIFICADO
Garza Montes de Oca, Nelson FedericoNO ESPECIFICADONO ESPECIFICADO
Monsalve G., AlbertoNO ESPECIFICADONO ESPECIFICADO
Mena, JuanNO ESPECIFICADONO ESPECIFICADO
Seco, RodrigoNO ESPECIFICADONO ESPECIFICADO
Fecha del depósito: 27 Mayo 2019 15:36
Última modificación: 26 Mayo 2020 20:45
URI: http://eprints.uanl.mx/id/eprint/14994

Actions (login required)

Ver elemento Ver elemento

Downloads

Downloads per month over past year