Estudio del mecanismo de eliminación demagnesio de aleaciones Al-Si en estado líquido mediante inyección de minerales base sílice

Muñoz Arroyo, R. y Escobedo Bocardo, J. C. y Hernández García, H. M. y Cortés Hernández, D. A. y Terrones Maldonado, M. y Rodríguez Pulido, A. y Hernández Piñero, J. L. (2010) Estudio del mecanismo de eliminación demagnesio de aleaciones Al-Si en estado líquido mediante inyección de minerales base sílice. Revista de Metalurgia, 46 (4). pp. 351-359. ISSN 0034-8570

[img]
Vista previa
Texto
743.pdf - Versión Publicada
Available under License Creative Commons Attribution Non-commercial No Derivatives.

Download (4MB) | Vista previa
URL o página oficial: http://doi.org/10.3989/revmetalm.0949

Resumen

RESUMEN Se empleó el método de inyección sumergida de polvos por medio de un gas de arrastre inerte (Ar) con el fin de eliminar el magnesio de la aleación Al-Si A380 a 750 °C. Los polvos inyectados al baño de metal fundido fueron zeolita mineral, arena sílice y mezclas de ambas. Las variables de respuesta medidas fueron el contenido de magnesio en el baño metálico respecto al tiempo de inyección y las mermas de metal al final de cada experimento. En el análisis de resultados, la mezcla sílice:zeolita 66:34 % e.p. obtuvo la mayor eficiencia, lográndose una disminución en el contenido de magnesio en el baño metálico de 1 a 0.0066 % e.p. Los productos de reacción se analizaron por difracción de rayos-X, microscopía electrónica de barrido y de transmisión. Los resultados de estos análisis y el empleo del paquete termodinámico FactSage, versión 6, permitieron justificar el mecanismo de reacción entre los minerales y el aluminio líquido. ABSTRAC In order to eliminate magnesium from an A 380 Al-Si alloy at 750°C, the submerged powder injection method, using an inert carrier gas (Ar), was applied. The injected powders in the liquid aluminum bath were zeolite, silica and mixtures of zeolite-silica minerals. For each experiment the response variables were: eliminated magnesium versus injection time and quantity of drosses produced. Chemical analysis by atomic absorption spectrometry showed that mixtures of silica-zeolite 66:34 wt% have the best results with regarding to the removal magnesium from 1 to 0.0066 wt%. During the elimination of magnesium complex stoichiometry compounds were formed due to the reactions among zeolite, water steam and liquid aluminum. These compounds were analyzed by XRD, SEM and TEM. The results obtained, along with using the FactSage 6 thermodynamic software, allowed to elucidate the reaction mechanism between the minerals used and liquid aluminum.

Tipo de elemento: Article
Palabras claves no controlados: Zeolita; Sílice; Aluminio; Magnesio; Minerales.
Usuario depositante: Lic. Josimar Pulido
Creadores:
CreadorEmailORCID
Muñoz Arroyo, R.NO ESPECIFICADONO ESPECIFICADO
Escobedo Bocardo, J. C.NO ESPECIFICADONO ESPECIFICADO
Hernández García, H. M.NO ESPECIFICADONO ESPECIFICADO
Cortés Hernández, D. A.NO ESPECIFICADONO ESPECIFICADO
Terrones Maldonado, M.NO ESPECIFICADONO ESPECIFICADO
Rodríguez Pulido, A.NO ESPECIFICADONO ESPECIFICADO
Hernández Piñero, J. L.NO ESPECIFICADONO ESPECIFICADO
Fecha del depósito: 29 Abr 2019 18:44
Última modificación: 29 Abr 2019 18:44
URI: http://eprints.uanl.mx/id/eprint/15081

Actions (login required)

Ver elemento Ver elemento

Downloads

Downloads per month over past year