High strain rate characterization of thermoplastic fiber-reinforced composites under compressive loading

Ramírez Montes, Carolina y Reis, Vitor y Opelt, Carlos y Santiago, Rafael y Almeraya Calderón, Facundo y Donadon, Mauricio V y Gaona Tiburcio, Citlalli y Croche, René y Baltazar Zamora, Miguel Ángel (2019) High strain rate characterization of thermoplastic fiber-reinforced composites under compressive loading. In: Aerospace engineering. Intechopen, Reino Unido, pp. 1-24. ISBN 9781839627873

Vista previa

Texto 24982.pdf - Versión Publicada Available under License Creative Commons Attribution Non-commercial No Derivatives. Download (6MB) | Vista previa

Resumen

Experimental study on the mechanical behavior of polyphenylene sulfide (PPS)-based composite laminates reinforced with carbon and glass fibers subjected to different strain rates under compression load is reported. Quasi-static tests have been carried out using an electromechanical universal testing machine at three different strain rates, while dynamic tests were done using a split-Hopkinson pressure bar (SHPB) apparatus at two pressure setups in the gas chamber. High-speed imaging system was used to monitor failure process during dynamic test, and these images were used to measure strain by digital image correlation (DIC) in order to compare the DIC-based measurements performed with the SPHPB strain gauges and quasi-static results. Fractography analysis was also performed to identify the main failure mechanisms induced at different strain rates.

Tipo de elemento:	Sección de libro.
Palabras claves no controlados:	High strain rate, Thermoplastic fiber-reinforced composites, Fractography
Materias:	CONACYT > Ingeniería y Tecnología T Tecnología > TA Ingeniería General y Civil
Divisiones:	Ingeniería Mecánica y Eléctrica
Usuario depositante:	Dra Citlalli Gaona
Creadores:	Creador Email ORCID Ramírez Montes, Carolina NO ESPECIFICADO NO ESPECIFICADO Reis, Vitor NO ESPECIFICADO NO ESPECIFICADO Opelt, Carlos NO ESPECIFICADO NO ESPECIFICADO Santiago, Rafael NO ESPECIFICADO NO ESPECIFICADO Almeraya Calderón, Facundo NO ESPECIFICADO orcid.org/0000-0002-3014-2814 Donadon, Mauricio V NO ESPECIFICADO NO ESPECIFICADO Gaona Tiburcio, Citlalli citlalli.gaonatbr@uanl.edu.mx orcid.org/0000-0001-9072-3090 Croche, René NO ESPECIFICADO NO ESPECIFICADO Baltazar Zamora, Miguel Ángel NO ESPECIFICADO NO ESPECIFICADO
Fecha del depósito:	08 Mar 2023 21:09
Última modificación:	16 Mar 2023 22:43
URI:	http://eprints.uanl.mx/id/eprint/24982

Actions (login required)

Ver elemento