Corrosion behavior of AISI 409Nb stainless steel manufactured by powder metallurgy exposed in H2SO4 and NaCl solutions

Cabral Miramontes, José Ángel y Barceinas Sánchez, J.d.O y Poblano Salas, Carlos y Pedraza Basulto, G. K. y Nieves Mendoza, Demetrio y Zambrano Robledo, Patricia del Carmen y Almeraya Calderón, Facundo y Chacón Nava, José G. (2013) Corrosion behavior of AISI 409Nb stainless steel manufactured by powder metallurgy exposed in H2SO4 and NaCl solutions. International journal of electrochemical science (8). pp. 564-577. ISSN 1452-3981 (Entregado)

[img]
Vista previa
Texto
199.pdf - Versión Publicada
Available under License Creative Commons Attribution Non-commercial No Derivatives.

Download (1MB) | Vista previa
URL o página oficial: http://www.electrochemsci.org/

Resumen

Powder metallurgy is an effective method for manufacturing stainless steel parts of high quality and accuracy at low cost. However, the use of sintered stainless steels is limited due to their low density, which deteriorates their corrosion resistance. The aim of this study was to determine the corrosion behavior of AISI 409Nb stainless steel specimens sintered with different contents of boron in a hydrogen atmosphere. Boron was added for promoting the formation of a liquid phase during sintering at 1150 °C, thereby achieving a reduction of porosity and increase in density, which is necessary to improve corrosion resistance. The electrochemical techniques of linear polarization resistance (LPR) and electrochemical noise (EN) were used to determine the corrosion behavior of samples with and without additions of boron after immersion in two solutions, 0.5M H2SO4 and 0.5M NaCl. The corrosion rates and the possible corrosion mechanisms in the sintered samples were determined. The results indicate that the samples with boron additions are more prone to corrosion due to chromium carbide precipitation.

Tipo de elemento: Article
Palabras claves no controlados: Boro, Fase líquida, Pulvimetalurgia, Sinterización, Ruido electroquímico.
Materias: T Tecnología > TN Ingeniería Minera. Metalurgia
Divisiones: Ingeniería Mecánica y Eléctrica
Usuario depositante: Editor Repositorio
Creadores:
CreadorEmailORCID
Cabral Miramontes, José ÁngelNO ESPECIFICADONO ESPECIFICADO
Barceinas Sánchez, J.d.ONO ESPECIFICADONO ESPECIFICADO
Poblano Salas, CarlosNO ESPECIFICADONO ESPECIFICADO
Pedraza Basulto, G. K.NO ESPECIFICADONO ESPECIFICADO
Nieves Mendoza, DemetrioNO ESPECIFICADONO ESPECIFICADO
Zambrano Robledo, Patricia del Carmenpatricia.zambranor@uanl.edu.mxNO ESPECIFICADO
Almeraya Calderón, Facundofacundo.almerayacl@uanl.edu.mxorcid.org/0000-0002-3014-2814
Chacón Nava, José G.NO ESPECIFICADONO ESPECIFICADO
Fecha del depósito: 22 Jul 2023 21:15
Última modificación: 22 Jul 2023 21:15
URI: http://eprints.uanl.mx/id/eprint/25624

Actions (login required)

Ver elemento Ver elemento

Downloads

Downloads per month over past year