Abrasive wear in hard thin films coated dies in hot extrusion aluminum

Herrera, J. y Martinez, D. y González, R. y Rodriguez, J. (2012) Abrasive wear in hard thin films coated dies in hot extrusion aluminum. Química Hoy, 2 (2).

[img]
Vista previa
PDF
Art1.pdf

Download (6MB) | Vista previa

Resumen

Abrasive wear resistance ofbat extrusionAISI H13 coated dies used to produce extruded aluminum micro multivoid tubes was studied. In this process, aluminum and dies are constantIy under high friction conditions producing prematuTe die wear; aluminum or lubricant adherence on die surface layer, is caused by this phenomenon with product rejection as a consequence. The hot ex1rusion dies most important properties are hot hardness, wear resistant and surface finishing. Extrusion dies coated witb. hard thin film coatings by physical vapor deposition. PVD and chemical vapor deposition, CVD, were utilized and thermal diffusion treatment as 3D alternative. The thin film coatings mechanical propemes, nano indentation, and SEM surface anaIysis were performed to characterize coatings and dies. Thc wear mcchanism was dctcrmined and it is affected by the die contact surface layer finished by electropolishing and the dies coated with thermal diffusion treatment was the most resistant condition to the wear process due to the presence of V andNb carbonitrures

Tipo de elemento: Article
Materias: Q Ciencia > Q Ciencias en General
Q Ciencia > QD Química
Divisiones: Ciencias Químicas
Usuario depositante: Admin Eprints
Creadores:
CreadorEmailORCID
Herrera, J.NO ESPECIFICADONO ESPECIFICADO
Martinez, D.NO ESPECIFICADONO ESPECIFICADO
González, R.NO ESPECIFICADONO ESPECIFICADO
Rodriguez, J.NO ESPECIFICADONO ESPECIFICADO
Fecha del depósito: 07 Jun 2013 23:15
Última modificación: 24 Nov 2014 16:27
URI: http://eprints.uanl.mx/id/eprint/2977

Actions (login required)

Ver elemento Ver elemento

Downloads

Downloads per month over past year