Experimental study of the influence of stitched nylon threads in glass-fiber-reinforced polymer two-dimensional multilayer composite on tensile strength

Lira Martínez, Manuel Alejandro y Gaona Tiburcio, Citlalli y Almeraya Calderón, Facundo y Jáquez Muñoz, Jesús Manuel y Zalapa Garibay, Manuela Alejandra (2023) Experimental study of the influence of stitched nylon threads in glass-fiber-reinforced polymer two-dimensional multilayer composite on tensile strength. Applied Sciences, 13 (21). p. 11679. ISSN 2076-3417

Vista previa

Texto
30164.pdf - Versión Publicada
Available under License Creative Commons Attribution Non-commercial No Derivatives.
Download (6MB) | Vista previa

Resumen

Stitched filaments are known to modify the mechanical properties of glass-fiber-reinforced polymers 2D (GFRPs 2D), so studying the effect on mechanical properties is underway to determine the critical variables involved. This research focuses on the study of the tensile strength effect of stitched low-density Barkley FBA BGQS15-15 nylon monofilament on biaxial E-Glass Saertex 830 g/m2 (+/−45◦) cured with Polyester Sypol Resin 8086 CCP using a vacuum infusion process. Four specimens were made with longitudinal distances between the stitched reinforcements of 0.5, 1.0, 1.5, and 2.0 cm, respectively. Tensile strength tests based on standard ASTM D3039 were performed to study how stitching can affect toughness, Young’s modulus, deformation, ultimate strength, and yield strength. The results indicated that the stitching increases Young’s modulus up to 99.2%, UTS is increased by up to +3.14%, deformation decreases by up to −41.66%, and toughness decreases by up to −36.89%. Although the stitching’s main function is to increase interlaminar resistance, it also induces the formation of stress concentrations by the new threads, and premature failure in the matrix was shown.

Tipo de elemento:

Article

Palabras claves no controlados:

Composite, Delamination, Laminated, Tensile, Interlaminar, Fiberglass, Polyester

Divisiones:

Ingeniería Mecánica y Eléctrica

Usuario depositante:

Editor Repositorio

Creadores:

Creador	Email	ORCID
Lira Martínez, Manuel Alejandro	NO ESPECIFICADO	NO ESPECIFICADO
Gaona Tiburcio, Citlalli	citlalli.gaonatbr@uanl.edu.mx	orcid.org/0000-0001-9072-3090
Almeraya Calderón, Facundo	facundo.almerayacl@uanl.edu.mx	orcid.org/0000-0002-3014-2814
Jáquez Muñoz, Jesús Manuel	NO ESPECIFICADO	NO ESPECIFICADO
Zalapa Garibay, Manuela Alejandra	NO ESPECIFICADO	NO ESPECIFICADO