Electrochemical Noise Analysis in Passivated Martensitic Precipitation-Hardening Stainless Steels in H2SO4 and NaCl Solutions

Almeraya Calderón, Facundo y Gaona Tiburcio, Citlalli (2025) Electrochemical Noise Analysis in Passivated Martensitic Precipitation-Hardening Stainless Steels in H2SO4 and NaCl Solutions. Metals, 15 (8). pp. 1-20. ISSN 2075-4701

[img]
Vista previa
Texto
metals-15-00837.pdf

Download (5MB) | Vista previa
URL o página oficial: https://doi.org/10.3390/met15080837

Resumen

Precipitation-hardenable stainless steels (PHSS) are widely used in various applications in the aeronautical industry such in as landing gear supports, actuators, and fasteners, among others. This research aims to study the pitting corrosion behavior of passivated martensitic precipitation-hardening stainless steel, which underwent passivation for 120 min at 25 ◦C and 50 ◦C in citric and nitric acid baths before being immersed in solutions containing 1 wt.% sulfuric acid (H2SO4) and 5 wt.% sodium chloride (NaCl). Electrochemical characterization was realized employing electrochemical noise (EN), while microstructural analysis employed scanning electron microscopy (SEM). The result indicates that EN reflects localized pitting corrosion mechanisms. Samples exposed to H2SO4 revealed activation–passivation behavior, whereas those immersed in NaCl exhibited pseudo-passivation, indicative of an unstable oxide film. Current densities in both solutions ranged from 10−3 to 10−5 mA/cm2, confirming susceptibility to localized pitting corrosion in all test conditions. The susceptibility to localized attack is associated with the generation of secondary oxides on the surface.

Tipo de elemento: Article
Palabras claves no controlados: corrosion; passivation; martensitic stainless steel; electrochemical noise
Materias: CONACYT > Ingeniería y Tecnología
T Tecnología > TJ Ingeniería Mecánica
T Tecnología > TN Ingeniería Minera. Metalurgia
T Tecnología > TP Tecnología Química
Divisiones: Ingeniería Mecánica y Eléctrica > Doctorado en Ciencias de la Ingeniería Aeronáutica
Usuario depositante: Dra Citlalli Gaona
Creadores:
CreadorEmailORCID
Almeraya Calderón, Facundofacundo.almerayacl@uanl.edu.mxorcid.org/0000-0002-3014-2814
Gaona Tiburcio, Citlallicitlalli.gaonatbr@uanl.edu.mxorcid.org/0000-0001-9072-3090
Fecha del depósito: 25 Ago 2025 21:05
Última modificación: 25 Ago 2025 21:05
URI: http://eprints.uanl.mx/id/eprint/30336

Actions (login required)

Ver elemento Ver elemento

Downloads

Downloads per month over past year